Isothermal Sections of the Ni-Cr-Ta Ternary System at 1200 °C and 1300 °C

Two isothermal sections of the Ni-Cr-Ta ternary system at 1200 °C and 1300 °C have been determined by using electron probe microanalysis, energy dispersive spectroscopy and differential scanning calorimeter. A Laves phase (Ni, Cr)2Ta(HT)(C14 structure) with large solid solubility stabilized by the Ni addition was determined in both two isothermal sections. The composition range of this phase was about 25.8–66.0 at.% Cr, 2.5-44.3 at.% Ni, and 24.0-40.0 at.% Ta at 1200 °C, which increased with raising temperature. The melting point of the Ni-Cr alloys decreased with the addition of Ta. No ternary compound was found in both these two isothermal sections. The present work could be significant for practical application of nickel-based alloys and future thermodynamics assessment of the Ni-Cr-Ta ternary system.

Abstract licence: CC BY

38 more references, whose wording the paper’s licence keeps private.

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.