Grain Size Effect on the Mechanical Behavior of Metastable Fe-23Cr-8.5Ni Alloy

An Fe-23Cr-8.5Ni alloy was used as a model material to study the grain size effect on the mechanical behavior of metastable duplex metal. Alloy samples with different grain sizes ranging from 0.1 to 2 μm were prepared by cold-rolling and annealing. A structural refinement to about 0.1 μm results in a high yield strength but very limited ductility. A significant improvement of ductility occurred at the grain size of about 0.4 μm. A further increase in grain size results in a decreased strength and a slightly improved ductility. The alloy with a grain size of about 0.4 μm exhibits an excellent combination of strength and ductility, where the yield strength and tensile elongation are increased up to 738 MPa and 29% as compared to 320 MPa and 33% of a coarse-grained (about 2 μm) sample, respectively. The origin of the excellent mechanical properties was attributed to the unique deformation characteristics associated with the transformation induced plasticity and the development of back stress.

Abstract licence: CC BY

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.