Study of Formed Oxides in IN718 Alloy during the Fabrication by Selective Laser Melting and Electron Beam Melting

This study confirmed that Al2O3 particles were formed in IN718 alloys during the fabrication by both selective laser melting (SLM) and electron beam melting (EBM). Different heat pattern and atmospheres in SLM and EBM result in different distribution and volume fraction of Al2O3 particles. The Al2O3 oxides would act as nucleation sites for the precipitation of Nb/Ti carbides, leading to the formation of unique core-shell composites with Al2O3 in the center and Ti/Nb at the periphery. In order to investigate the oxygen content introduced during SLM and EBM, the volume fraction of Al2O3 formed in spark plasm sintering (SPS)-fabricated substrate, by consolidating the pre-oxidized IN718 raw powders at 800 °C, was utilized. The oxygen contents introduced to IN718 substrates during SLM and EBM fabrication were calculated to be 0.030 wt% and 0.099 wt%, respectively.

Abstract licence: CC BY

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.