Investigation on Fracture of a 6014-T4 Aluminum Alloy Sheet in the Flanging and Hemming Process Based on Numerical and Experimental Methods

The fracture of a flat-surface straight-edge hemmed component of aluminum alloy sheets was investigated in this study. The specimen was made of 1 mm thick 6014-T4. Natural aging characteristics of 6014-T4 were studied via uniaxial tensile tests. The results show that the yield stress and ultimate tensile strength increased while the uniform elongation, strain hardening exponent, and plastic strain ratio decreased during the natural aging period, which worsened the formability. The sheet was biaxially stretched to obtain a pre-strain before the flanging and hemming operation. The influence of the flanging radius on the fracture was evaluated using experimental and numerical methods, and the optimum values were obtained. The comparison between the roller hemming and die hemming process proved that the former tends to produce better formability.

Abstract licence: CC BY

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.