Printability and Cell Viability in Extrusion-Based Bioprinting from Experimental, Computational, and Machine Learning Views

Ali Malekpour, Xiongbiao Chen

Journal of Functional Biomaterials · 2022 · Review · CC BY

doi:10.3390/jfb13020040

Abstract

Extrusion bioprinting is an emerging technology to apply biomaterials precisely with living cells (referred to as bioink) layer by layer to create three-dimensional (3D) functional constructs for tissue engineering. Printability and cell viability are two critical issues in the extrusion bioprinting process; printability refers to the capacity to form and maintain reproducible 3D structure and cell viability characterizes the amount or percentage of survival cells during printing. Research reveals that both printability and cell viability can be affected by various parameters associated with the construct design, bioinks, and bioprinting process. This paper briefly reviews the literature with the aim to identify the affecting parameters and highlight the methods or strategies for rigorously determining or optimizing them for improved printability and cell viability. This paper presents the review and discussion mainly from experimental, computational, and machine learning (ML) views, given their promising in this field. It is envisioned that ML will be a powerful tool to advance bioprinting for tissue engineering.

Full text

From PubMed Central, U.S. National Library of Medicine, as current on Oct 24, 2026. Paragraph numbers are ours, so an answer can point at one.

1. Introduction

During the last decade, the demand for organ transplantation has increased all over the world because of rising success in post-transplant results. Unfortunately, inadequate organs for transplantation to meet existing demands have led to a huge organ shortage crisis. Tissue engineering, as a combination of biology, engineering, and material science, is a promising field that can obviate this crisis by producing artificial tissue and organs. Tissue engineering has advantages over other therapies (e.g., the use of drugs) because of its ability to provide a lasting solution to the problem of organ failure. A scaffold is a porous construct used in tissue engineering to support cell growth and funcations. Several fabrication techniques have been developed and used to fabricate scaffolds, and in general, these techniques can be divided into conventional, electrospinning, and three-dimensional (3D) printing. Further, 3D printing can be categorized into inkjet, laser-assisted, and extrusion-based bioprinting. Nowadays, extrusion-based bioprinter is one of the most popular techniques in biomedical applications because of its ability to print cells, and various biomaterials with a wide range of viscosity.

Biomaterials with living cells (or bioinks) or biomaterials without cells (inks) are printed to form constructs or scaffolds. To this end, the biomaterials must have such characteristics as (a) biocompatibility, (b) biomimicry, (c) mechanical integrity, (d) degradability, and (e) printability. With 3D printing, it is expected that the printed scaffolds can mimic the structures, properties, and functions of particular organs for tissue engineering. Hence, the keys are the printing of scaffolds and their culture for maturation to functional constructs. For the printing of scaffolds, the printability of the chosen biomaterials must be considered before the printing process because of the differences seen between printed scaffolds and the designed ones. Although incorporating cells with biomaterial is a promising advance in bioprinting, cells might be affected and even damaged during the printing process. Cell viability is another vital issue needed to be considered. For this, numerous studies have been conducted to fabricate biomimetic scaffolds with preserved cell viability in the extrusion-based bioprinting process. As the evaluation and optimization of printing parameters intended to achieve the improved printability and cell viability through trial and error was expensive and time consuming, computational methods came to play a role. Nowadays, with the advent of supercomputers, machine learning (ML) has depicted a new view for many fields of science and engineering, including biofabrication, with many promising results. It is envisioned that ML can accelerate bioprinting development. This paper aims to review printability and cell viability from experimental, computational, and machine learning perspective.

2.1. Printability

Generally, the printed construction may not be the same as the designed one. Sometimes, the printed structure collapses and cannot keep its stability. The printed biological product must mimic the architecture and shape of an organ, so the printing needs to be precise with high resolution and shape fidelity. The concept of printability refers to the ability to form a 3D structure with acceptable fidelity and integrity. Printability demonstrates its critical role when the tissue of an intricate organ such as the heart is required. In addition to function, geometry is very important. There are various definitions for printability based on employed techniques for printing. Printability in the inkjet approach is recognized as the ability to generate well-defined droplets in the air. In laser-based printing, printability refers to the ability to produce a well-defined jet, form appropriate droplets, and deposit them onto the receiving substrate. For extrusion bioprinting, printability characterizes the capability to print continuous filaments with controllable diameter and defined morphology to form desired 3D structure.

2.1.1. Evaluation of Printability

It is necessary to define indexes to characterize printed constructs in terms of printability. It is noted that a bioink needs to have appropriate shear thinning behaviour with low viscosity when being printed and recovered or high viscosity for stability after printing. To evaluate the printability of bioink, Paxton et al. suggested a two-step method. First, this method focuses on screening ink formulation to assess filament formation and the ability to form 3D structure, and the second step is the rheological evaluation of inks to assess yield point, shear thinning, and recovery behaviour via shear stress ramp, shear viscosity, and recovery test, respectively. There are different definitions for printability indexes. The most popular ones are reviewed as follows:Extrudability: the minimum extrusion pressure required to print material at the desired flow rate;Strand printability:This factor is used to compare printed strands dimeters with CAD-generated parameters strands. The expected strand diameter is: where DS, Vn, and Qt are strands diameter, needle speed, and volumetric flow rate, respectively.So, needle speed affects the diameter of strands, and the below index is defined to compare printed strands with calculated ones:Integrity factor: this factor compares the thickness of printed scaffolds and designed ones Irregularity:In fact, this index is developed index of integrity in 3 dimensions. It compares the outer geometry of scaffolds with designed ones in X, Y, and Z directions:Pore printability:In addition to printability indexes such as irregularity and integrity factors which are based on the outer geometry of scaffolds, the pore printability index focuses on internal geometry. This index is utilized to determine how printed pores matched the designed square ones in a scaffold:

Extrudability: the minimum extrusion pressure required to print material at the desired flow rate;

Strand printability:

This factor is used to compare printed strands dimeters with CAD-generated parameters strands. The expected strand diameter is: where DS, Vn, and Qt are strands diameter, needle speed, and volumetric flow rate, respectively.

So, needle speed affects the diameter of strands, and the below index is defined to compare printed strands with calculated ones:

Integrity factor: this factor compares the thickness of printed scaffolds and designed ones

Irregularity:

In fact, this index is developed index of integrity in 3 dimensions. It compares the outer geometry of scaffolds with designed ones in X, Y, and Z directions:

Pore printability:

In addition to printability indexes such as irregularity and integrity factors which are based on the outer geometry of scaffolds, the pore printability index focuses on internal geometry. This index is utilized to determine how printed pores matched the designed square ones in a scaffold:

2.1.2. Effective Parameters on Printability

Various parameters play a key role in extrusion bioprintability that can be categorized into three groups: bioink properties, printing parameters, and design construct.

Bioink Properties

Bioinks may contain hydrogels, decellularized matrix components, tissue spheroids, cell pellets, or some advanced bioinks. The most popular class of biomaterials are hydrogels because of their capacity to provide a viable environment for the adhesion, growth, and proliferation of living cells. The main feature of hydrogels is their ability to absorb and retain large quantities of water. Hydrogels are non-Newtonian fluids with shear thinning and thixotropic behaviour, which are suited for the extrusion process. The shear thinning enables the shear force to align the random polymer chains in a favourable direction and makes them extrudable. Thixotropy, a time-dependent shear thinning behaviour, makes the hydrogels exhibit low viscosity during printing and regain stability after extrusion.

Rheological property is a critical key to the printability of hydrogels, and viscoelasticity is a conclusive factor in bioprinting. Printing low viscous materials leads to soft and watery structures; however, printing high viscous materials is difficult to extrude. Examining the relationship between shear stress and viscosity under embedded shear rate provides applicable information for the printability of bioinks.

Differences between printing techniques have led to requiring different properties of hydrogels. For example, extrusion-based and inkjet-based systems utilize nozzles to deposit biomaterials. They require appropriate rheological properties, and the most important one is viscosity. In fact, extrusion-based bioprinting is a modification of inkjet printing that can print uninterrupted strands instead of a single droplet. This printing technique can print almost all types of hydrogels with varying viscosity depending on the dispensing force system. Among extrusion approaches, a pneumatic system powered by pressurized air can support a wider range of viscosity but has difficulty precisely controlling deposited mass. Screw-based ones are cheaper but have problems with high viscous materials.

The viscosity of the hydrogel is an effective parameter for printability; however, it cannot capture the complicated behaviour of bioink, and a high viscous hydrogel does not guarantee precise printing. Dynamic modulus, including storage modulus (G′) and loss modulus (G″), can describe the bioink behaviour better. The loss tangent (G″/G′) is another parameter that makes the biomaterial behave more like a solid or a liquid. A small loss tangent refers to a material with more solid behaviour, high stiffness, and good mechanical properties which can maintain its designed shape and require larger extrusion pressure. On the other hand, a large loss tangent represents highly fluid behaviour, easily extrudable material without adequate mechanical strength to hold the structure.

In addition to the flow behaviour of the bioink, surface tension is another physical property needed to be considered in extrusion bioprinting. At the liquid—air interface, surface tension appears because of the attraction force between liquid molecules rather than the attraction between liquid and air, thus affecting the profile or contour formed on the surface. Surface tension is usually studied in inkjet-based printing, and its effect on printability is neglected in extrusion-based bioprinters.

Surface tension appears as a contact angle between two media and plays a key role in the printed strands and printing resolution. If the substrate has higher surface energy rather than the bioink surface tension, the ink will spread. In contrast, less substrate energy results in a higher contact angle and less spread.

Bioprinting Parameters

An extrusion bioprinter commonly consists of three main units: a container (e.g., syringe) containing biomaterials, a dispensing head that derives biomaterial out, and a receiving stage where the bioink is collected. The parameters that control those three units and involve the printing process can affect accuracy and printing resolution (resolution is the smallest achievable diameters of strands). In this matter, many investigations have reported that nozzle diameter, speed of the dispensing head, height of the nozzle, and flow rate of extruded bioink can affect the width and height of the printed strands. The aforementioned variables must be balanced to achieve the desired printed strands with a uniform diameter and high pattern fidelity.

Dispensing pressure is the most important parameter in extrusion-based systems. Pressure should be large enough to overcome the ink surface tension for pushing the ink out of the nozzle. Under low pressure, hydrogels may not be driven to flow, while jetting would happen over high pressure. Obviously, there is a direct relationship between dispensing pressure, flow rate, and strands diameter.

High flow rate, low needle linear speed, and high distance between the needle tip and the collector can result in thicker strands and a material bugle at the front edge of the needle (Figure 1b). In contrast, a low flow rate and a very slow needle movement cause a gap between the needle tip and stage (Figure 1c).

The diameter of the needle is another important factor. Obviously, a lower diameter-needle can print a construction with high resolution (Figure 1), but clogging of the needle and high dispensing pressure are two limitations that should be considered. By increasing the concentration of the bioink, a needle with a higher diameter is preferred; however, needle temperature can improve the viscosity when high concentration bioinks are printed, especially for thermal-sensitive biomaterials.

During and after printing, to achieve the desired mechanical integrity and shape, the bioink must be solidified and cross-linked. Both materials and cross-linking agents should be prepared to reach appropriate viscosity, yield stress, and mechanical integrity for fast shear recovery. Among cross-linking methods, adjusting the temperature of thermosensitive hydrogels (e.g., gelatin), using cross-linking agents, and ultraviolet light can be mentioned.

There are some other key parameters such as distance between nozzle and substrate, substrate temperature and the angle of printing on the corners. As can be seen in Figure 2, the overlap problem in sharp angle during printing is a common issue that must be avoided. Printing resolution became worse in acute angles rather than obtuse ones at the same printing parameters, and it might cause nonuniform layer height in the 3D structures. There are two ways to avoid nonuniform extrusion. The first is to avoid the sharp angles in the printing, although sometimes sharp angles due to the complexity of the structure are inevitable. The second method is reducing the flow rate of bioink in this area to half or doubling the dispensing speed.

Construct Design

Filament spacing and filament orientation are two critical parameters in the matter of construct design that influence printability. Filament spacing affects pore sizes and the subsequent integrity and fidelity of the construct. A small filament spacing can lead to the fusion of adjacent filaments if the bioink has low viscosity and a small contact angle (Figure 3a). On the other hand, large spacing may result in a large over-hanger deflection (Figure 3b).

The orientation of strands makes the configuration and inner pattern of the scaffolds and, subsequently, the porosity. The orientation of strands near the edge of the scaffold affects the amount of bioink deposited. To illustrate, an orientation of 45° requires less amount of bioink than 90°

2.1.3. Printability Improvement

The formulation of the ink with suitable rheological, biological, and mechanical properties are crucial aspects of the bioprinting process. The strategies for printability enhancement are related to the mentioned effective parameters (i.e., bioink properties, printing process, design). Table 1 lists the biomaterials commonly used in extrusion bioprinting owing to their appropriate rheological, mechanical, and biological properties. From these biomaterials, researchers have further synthesized composite biomaterials for their property synergy and improved printability.

There is a huge number of studies that evaluate various types of bioinks—a mixture of cells and biomaterials—to improve printability. As a good example, twelve types of hydrogels, including collagen, chitosan, fibrin, alginate, etc., were studied. Hydrogels were oriented over a 1 cm2 target printing area, and printing accuracy was calculated. MC-HA, chitosan, and chitosan–collagen gels were the most accurately printed ones because the relatively high viscosity of the solutions inhibited them from spreading out on the surface.

Alginate obtained from seaweed and algae forms a promising hydrogel for tissue engineering applications because of its inherent nature. Regardless of appropriate compatibility, the main disadvantage of alginate is the formation of unstable gels at lower concentrations because of low viscosity. Although by varying the concentration and molecular weight of alginate, the viscosity could be increased, to overcome this problem and extrude filaments with well-defined morphology, gelatin can be added into the bioink. Combining alginate with high molecular weight molecules like nanofibrillated cellulose also enhances the resolution of printed filaments. Mouser et al. added gellan into gelatin gum methacrylate (GelMA) to increase the viscosity and gelation speed of the hydrogel because printing GelMA on its own requires high concentration and precise control of the ink, nozzle, and receiving platform’s temperature.

To improve the printability of alginate, pre-cross-linked alginate with CaCl2 and a mixture of alginate and gelatin were printed and compared. The pre-cross-linked alginate was printed and formed a liquid-like scaffold with inconsistent pore diameters. In contrast, adding gelatin enhanced the printability of the ink significantly.

Adding additive biomaterials can change the rheology properties of hydrogels; for example, adding nanofibrillated cellulose (NFC) to alginate makes the bioink shear thinning with high fidelity. GelMA-based bioink is another common biomaterial used for extrusion bioprinting because of its photo-cross-linking ability.

Using a supportive scaffold is a strategy to enhance shape fidelity. To illustrate, a printed PCL scaffold is used as a support for alginate scaffolds in the bioprinting of alginate. These kinds of support can be sacrificial, especially for printing complex geometry. Lee et al., during printing poly-caprolactone (PCL) and cell-laden hydrogel, printed poly-ethylene-glycol (PEG) as a sacrificial layer to support the main structure. After finishing the process, PEG can be removed easily in an aqueous solution.

Among traditional implementation of printing techniques in an air medium, emerging technology is printing in a liquid bath or a hydrogel support bath medium. Printing in a support bath medium enables low viscous hydrogels to generate complex 3D structures. The limitations of printing in air, including clogging, gravity-induced structural collapse with weak interfacial strength, and the absence of a support structure, can be relieved using this approach. Specifically, low viscous materials minimize the occlusion of extrusion nozzles during printing within a support bath. The relationship between the diameter of strands and nozzle speed is similar to printing in the air. Increasing the flow rate by considering the constant filament’s diameter leads to higher nozzle speed and, subsequently, a less viscous environment for a shear thinning bath with large surface tension. This approach reduces irregularity and exhibits a smooth surface for the filaments.

To print a complex construct with different materials for each part, utilizing a multihead bioprinter might be applicable. The calibration of the different heads plays a critical role during multihead bioprinting. For example, Sodupe-Ortega et al. suggested two models for calibration of a four-head printer depending on its application. In the first model, adjusting the printhead’s xy position with respect to each other, they printed straight lines, half with one printhead and half with the other. In the second model for optimizing dispensing pressure and speed, a continuous zigzag pattern was printed with an increasing distance between all lines (Figure 4).

2.2. Cell Viability

The majority of the above studies were focused on the influence of various parameters on the printability of bioink; however, to achieve a successful 3D printing process, assessing different parameters’ effects on printability and cell viability at the same time is vital. The main advantage of extrusion bioprinting is the ability to incorporate cells with biomaterials, but it should be noted that cells are sensitive to environmental change. During the printing process, cells and biomaterials are extruded through a needle by force. Printing force can produce shear and extensional stresses. If these stresses exceed a certain threshold, they can breach cells membranes and damage them.

Shear stress has a critical influence on cell biology; to illustrate, shear stress enhances the maturation of some cells and increases stem cell differentiation. In contrast, shear stress as a factor that damages cells is inevitable in any dispensing process and should be considered in printing progress. Shear stress is the mechanical force that causes the shearing deformation of materials and cells along the plane parallel to the stress direction. Depending on cells’ sensitivity and the amount of shear stress experienced by cells, the cell damage can change up to almost 100% at high shear stress. The shear stress is directly influenced by dispensing pressure, nozzle diameter, and viscosity of the bioink, especially when the needle diameter is reduced with the aim of promoting printing resolution.

Viscosity is a measurement of resistance to flow; highly viscous solutions can increase shear stress during extrusion and lead to the rupture of the cell membrane. Printing high viscous bioinks requires high pressure, thus negatively affecting cell viability. It was reported that dispensing pressure more significantly affects cell damage compared with nozzle diameter.

The nozzle diameter and type have direct effects on cell viability. Smaller nozzle diameter leads to a higher velocity gradient as well as higher shear stress and, consequently, higher cell damage. Two types of needles, cylindrical and tapered, are commonly used in extrusion bioprinting. Because of their geometries, they have different effects; a tapered needle provides a higher flow rate than a cylindrical one under the same printing pressure. Indeed, for the same flow rate, lower printing pressure is required for tapered needles, thus preserving higher cell viability.

Nozzle and chamber temperatures are other effective factors in cell viability. By controlling the nozzle and chamber temperature, cell viability could be increased from 55.52% to 90%. In addition to thermal damage, the time period or the duration of printing must be considered during bioprinting. Long bioprinting time can reduce cell viability after extrusion. For improvement, hybrid polymer constructs made from mixing high and low melting temperatures were reported to recuse cell damage associated with temperature and bioprinting time. The concentration of the bioink can also influence cell viability. It was reported that concentrated polymers have adverse effects on cell culture. For instance, there were more dead cells for a higher concentration of alginate.

Mathematical modelling is a tool to represent the bioprinting process as well as the influence of related parameters. In this regard, cell viability laws have been developed to depict the relationship between shear stress and cell viability. If shear stress is considered one of the main causes of cell damage, the following power–law function is used to describe the cell damage percentage: where I is the percentage of cell damage, τ is the shear stress, and C and b are constants for given cells. This equation is developed further by considering the exposure time of cells to shear force: where I is the percentage of cell damage, τ is the shear stress, t is exposure time, C, a, and b are constants for given cells. This model has two drawbacks: First, this equation does not provide information about the probability distribution of cell damage with stress and exposure time and their correlation. Secondly, this equation is not applicable for a large range of stress or exposure time because, in this situation, the left side of the equation will be 100%. Li et al. improved this cell damage law by using a bivariate normal distribution function, and Nair et al. also defined a law to predict damaged cells and dead ones separately.

3. Computational View

Three-dimensional printing potentially can revolutionize biofabrication engineering. The printability of the ink must be evaluated to achieve desired printed construct. Experimental evaluation of the ink printability is time-consuming and costly, especially when bioink with expensive and sensitive cells is printed. In this endeavour, computational methods as powerful tools provide information to bridge gaps between knowledge when clinical testing is difficult, expensive, time-consuming, or even impossible.

3.1. Printability

Most of the printability simulations are in the field of inkjet bioprinting and droplet shapes. A study has been conducted to consider the influence of rheological properties of bioink on jetting behaviour during printing by an inkjet 3D printer. Computational fluid dynamic (CFD) has been employed through Flow 3D software to simulate rheological properties and droplet formation.

An investigation using the Continuum Surface Force (CSF) method for modelling surface tension and employing CFD-ACE+ commercial software investigated the effects of printing parameters on length tail, breaking time, and volume droplet. Another study demonstrated the feasibility of using CFD to predict dependencies between printing parameters such as printer nozzle geometry, operation pressure, and printing speed in the extrusion-based bioprinting process. The rheological properties of the hydrogels were determined through different experimental methods and compared with data predicted by the computational model. The hydrogel viscosity was not predicted reliably because shear rates occurring within the printing tip were higher than the viscosity measured by the rheometer. CFD also was used to predict the relationship between resolution and printing speed. The predicted strand width depends on the contact angle between substrate and hydrogels.

The CFD via “OpenFOAM” software was employed to investigate the dependence between hydrogel mass flux, different needles geometry, and operating pressure. Power–law model was used for modelling Non-Newtonian hydrogels, and the VOF method tracked the interface between ink and air. “IPS IBOFlow” commercial software also simulated printed strands. IBOFlow is an incompressible finite volume-based fluid flow solver based on Immersed Boundary Method. The rheology of the bioink was modelled by a linear PTT model, and the continuum surface force method modelled the surface tension. The simulation had an appropriate agreement with experimental results (Figure 5).

In the literature, because of the complexity of the simulation of printed strands, most studies have used commercial software and rarely discussed simulation methods. In this matter, a brief discussion about different methods to model multiphase fluid is found in the next part.

3.1.1. Implementation

To evaluate the printability of the bioinks through computational methods, understanding the printed strands’ shape, in other words, the location of the interface between bioink and the air, is crucial. In fact, this simulation is a free surface fluid simulation. The term free surface is technically used to describe an interface between a liquid and a second medium that does not apply pressure gradient or shear stress. Free surface falls within the category of a multiphase flow problem. Some of the more popular techniques to track the interface are as follows:

Surface Marker Techniques

This approach tracks the interface explicitly on a fixed mesh, marking the interface by connecting a set of massless particles. These markers are moved by the local advection velocity field, so their position (xn, yn, zn) can be obtained by integration from the initial position at time = 0: where u, v, and w are the fluid velocity in the Eulerian mesh at the time-dependent location of each marker.

Surface-Fitted Method

In this method, instead of markers, a mesh surface is attached to the interface, and the position and curvature of the interface are calculated. The main advantages of this approach are (a) a reduction in computer storage occupied by the interface markers, (b) ensuring a sharp interface, and (c) avoidance of partially filled cells (every cell is occupied by a fluid). Since the mesh and the interface are moving together, the mesh automatically tracks the interface, and the mesh system conforms to the shape and structure of the interface. The weakness of this method is sensitivity to the mesh.

The Volume of Fluid (VOF)

The volume of fluid is the most well-known method used to simulate multiphase flow. In this approach, the volume of fluid function, or colour function C, is used that represents the phase fraction. The volume fluid function where a cell is completely occupied by one phase (bioink/air) is unity and by another phase (air/bioink) is zero (Figure 6). According to this definition, the interface location is where the value of the colour function of the cells is between zero and unity. The main advantage of this approach is the accuracy in solving the interface equation without compromising the mass balance, and its weakness is difficulty with sharp interface and curvature. In addition, the implementation of this method in 3D cases is complicated.

As an example of showing how the colour function works in this method, density and viscosity can be calculated by the following relations: where subscripts 1 and 2 are related to phases one and two, respectively.

Obviously, by decreasing the interface thickness, the solution will be more accurate. At first, the initially prescribed topology of the interface is used to calculate the volume function of each cell. For this task, the location of volumes truncated by the interface for each cell is required. After providing velocity field by solvers through solving Navier–Stokes, the interface is reconstructed from the local volume fraction.

There are different methods to calculate volume fractions based on the topology of the interface. The first method was Simple Line Interface Calculation (SLIC), presented by Noh, which represents the interface by a horizontal and vertical rectangle. Piecewise Linear Interface Calculation (PLIC) is another method that approximates the interface in each cell by an inclined line.

Level Set Method

The level set method is very close to VOF with a difference in representing the interface function. This class of interface captures the works based on the definition of a continuous level set function. Its magnitude is calculated through the distance between each cell and the interface. The sign of the function can be positive or negative based on the cell being in phase 1 or 2 (bioink and air) and zero value for the cells on the interface. The main advantages of this method compared with other techniques include the ability to predict sharp interface and attractive simplicity of mathematical formulation. Mass loss due to numerical errors can be noted as a disadvantage.

Surface tension is the dominant physical property that demonstrates the behaviour of the bioink after printing and must be known. Free surface molecules have higher energy than those in bulk. For a droplet of a liquid on a surface without external forces, the shape with the lowest surface energy and subsequently the lowest surface energy is a sphere. When the surface of the separation is curved, the pressure near the surface is different in the two media. Surface pressure is proportional to the curvature k of the interface and the surface tension force directed toward the center of the curvature (higher pressure medium to lower pressure one). There are two ways to implement surface tension. One approach is applying surface tension as a boundary condition along the free surface. For a staggered mesh, interpolation is needed to ensure that the pressures at the free surface and center of cells are in correct relation. This technique is not appropriate because the cost of iterations at each time step is high, considering the time-step restriction due to stability issues. Another issue is the need for the exact location of the free surface for the next time step. However, some techniques such as VOF and level set can predict the interface location at the current time; this value is not known for the next time step. To address the mentioned obstacle, Brackbill has suggested a method called continuum surface force (CSF). In this method, instead of determining the exact location of the interface, surface tension is added to the Navier–Stokes Equations as a body force. By considering the interface between two inviscid fluids, the surface tension force can be written as below, where k (curvature) is taken as positive if the center of curvature is in the air. where σ is the surface tension coefficient of the bioink, k is the local curvature, with R1 and R2 being the principal radii of the surface curvature, and is the unit normal.

Finally, the surface tension force is calculated: where the tilde and bracket denote smoothed value and the difference between the maximum and minimum value, respectively.

The continuum surface stress method (CSS) is another method that, instead of computing the curvature of the interface and adding a force to the momentum equation, introduced surface tension as a correction to the momentum stress tensor. This approach is completely independent of the topology of the interface, and the main advantage of that is its ability to perform 3D simulations and looks promising for simulation of complex dynamics. The capillary pressure tensor T is defined: where I is the unit tensor and is the tensor product operator

3.2. Cell Viability

Experimental evidence shows the effects of nozzle geometry and bioink properties on cell viability; computational studies are helpful to gain more insight into this evidence. Researchers defined a model based on the deformation and elongation of the cell membrane. The model connected (1) cell survival as a function of cell membrane elongation, (2) membrane elongation and cell droplet size, and (3) the substrate properties. The cell membrane may increase up to five percent approximately without cell death, and larger elongation can lead to rupture of the membrane. A finite element simulation by COMSOL 4.0a software compared conical and cylindrical needle shapes on cell viability. The power–law equation was used to model non-Newtonian flow behaviour. The simulation showed that the highest shear stress was obtained for conical-shaped needles, but the cells withstand the stress just at a short region near the outlet of the needle. In cylindrical needles, a lower peak of shear stress occurs but in the long path of the needle (Figure 7).

A sudden change in the geometry of the flow causes a significant change in linear velocity, and s, extensional flow occurs. Some studies employing CFD and using Fluent commercial software demonstrated that cells undergo dramatic stretching and deformation in the extensional flow, leading to cell damage. Aguado et al. showed that by reducing the diameter from 3.17 mm to 0.185 with the extensional flow, the cell is deformed. The cell viability from 89.1% (just linear shear occurs) decreased to 58.7% (extensional and linear shear flows occur); therefore, the main parameter that damages cells is extensional shear stress.

Romo et al. employed CFD and OpenFoam software to simulate a series of experimental studies reported on the cell viability in a range of printing parameters such as pressure, nozzle shape (conical and cylindrical) and size, and material properties, to calculate maximum shear and optimize needle geometry. They found that the radius of the needle at the middle and outlet of conical needles play a key role in optimizing cell viability.

4. Machine Learning View

Machine learning is a promising technology that can optimize systems by using smarter and more effective use of materials, products, and services. Machine learning is a subset of artificial intelligence (AI) focusing on designing systems. This designing process works on learning and predictions based on previous experiences. In contrast to computer programing that relies on expert codes, machine learning techniques are trained to transform inputs to output via statistical relationships. Humans are usually able to find a relationship between output (Y) and a set of input (X). When the input variables and outputs range from X0 to Xn and Y0 to Yn, humans will be overwhelmed by the complexity. Computer algorithms can guess and approximate functions among them, and that is the task of ML models.

The most common machine learning methods include supervised, unsupervised, reinforcement learning, and deep learning. In supervised ML, more inputs and outputs are available, and the approximate function will be found. In an unsupervised model, the output is not given, and the algorithm must find its own outputs as a pattern, a cluster, or a relationship in the data (X0, X1, … Xn). Reinforced ML is another approach similar to the supervised one in which the inputs and output are given, and the algorithm must find the function between X and Y but through a dynamic interaction with another algorithm named environment. The environment rewards or punishes the main algorithm for making that more accurate. Deep learning is another method that employs a collection of algorithms with multiple hidden layers applied to a new dataset instead of dynamically adjusting the agent’s actions from the feedback. (Figure 8).

Although machine learning has been used for improving 3D printing (additive manufacturing) in various ways, such as process optimization, manufacturing defect detection, and accuracy analysis, it has not been employed as much as it should in 3D bioprinting. Undoubtedly, it significantly affects the future development of this field.

4.1. Printability

Biofabrication works in the field of automated generation of functional biological products. Most of the techniques used in biofabrication were developed when additive manufacturing developed. Recently, ML was added to this field to cover key aspects impacting the biofabrication process efficiency directly. It would be valuable during material preparation, model designing, process optimization and monitoring. Developed algorithms can assist designers in choosing ideal printing orientation and material preparation, reduce design time, and consequently improve printability.

Raberu et al. used machine learning as a novel method to evaluate printability quantitatively and optimize printing parameters. Ink concentration, temperature, driving pressure, needle speed, and platform temperature were considered as inputs (Figure 9). Printability was evaluated by printing scores based on two fundamental criteria: printing filament morphology during the extrusion process and pore architecture on later stacking (Figure 10).

Recognizing anomalies accurately in layer-by-layer bioprinted configurations is another potential task of ML in medical projects. A camera mounted at the side of the printhead captured images of each layer as raw data for the machine learning tool. Three major anomalies, including discontinuity (broken raster), irregularity (improper line width), and nonuniformity (unsmooth surface), were recognized in the first layer of printed structures. Machine learning could properly recognize the anomalies and optimize printing parameters based on them.

Shi et al. employed a multiobjective optimization method and artificial neural network with computational fluid dynamics to simulate droplet formation and flow behaviour in drop-on-demand printing. Printing Silicone elastomer via freeform reversible embedding (FRE) is challenging due to depositing a Newtonian ink within a Bingham plastic support. To achieve this goal, hierarchical machine learning (HML) was employed, and the results showed that it is an effective tool to optimize printability factors. Conev et al. used an ML-based framework, printing conditions and printing parameters to predict the quality of print as “low quality” or “high quality”. Two methods were applied: a direct classification-based approach was used to train a classifier to distinguish between low and high printing quality, and a regression model was employed to approximate the values of a printing quality metric.

Another research utilized machine learning to predict the printability of various mixtures of collagen and fibrin. The rheological properties of inks were measured by a rheometer. Shape fidelity of inks was observed after printing and the data used by machine learning algorithms. As a result of machine learning analysis, the printable ink should have a high G’ for high fidelity and low τy for extrusion. A relationship was obtained to predict printable ink with high G’ and low τy. The Schematic of the process can be seen in Figure 11.

4.2. Cell Viability

Despite the extensive experimental work carried out in extrusion-based bioprinting, a comprehensive view of individual and combined effective parameters on cell viability is not straightforward to achieve because of the various parameters. Different models of extrusion process have evolved from analytical models based on simplifying assumptions to using CFD to simulate complex flow behaviour and nozzles shape. Computational methods were used to optimize process parameters. Increasing computational power and rapid development of various algorithms are making data analysis techniques, such as machine learning, appropriate to address optimization challenges.

In the matter of employing ML to predict cell viability, little research has been reported. Reina-Romo et al. developed an in silico framework to assess the effect of nozzle geometry, printing pressure, and material properties on the maximum shear stress as some of the main causes of cell mortality. They used CFD via OpenFoam software to simulate various shapes of nozzle and extrusion conditions; then, the Gaussian process was utilized to analyze the data and identify parameters affected by shear stress and related cell viability. Unlike ANOVA, the Gaussian process not only estimates the importance of individual parameters but also the influence of parameters on the outcome of a model is predicted.

Lack of data is the main challenge of the machine learning process, so available databases in the literature can be used as raw data for this kind of research. To illustrate, a dataset of 617 instances corresponding to a cell viability value and a dataset of 339 instances regarding a filament diameter in extrusion-based bioprinting systems were collected from the literature and used to train algorithms (ML). Regression-based and classification-based ML models were employed to predict cell viability and filament diameter for printing cell-laden alginate and gelatin bioinks. The results indicated that the classification-based ML can predict cell viability with an accuracy of 70%. More data gathering with a focus on the printing parameters can strengthen the database to provide higher accuracy.

Various kinds of algorithms can be used in ML. A streolithography-based bioprinting study used ML to develop a predictive cell viability model by considering four critical parameters, including UV intensity, UV exposure time, gelatin methacrylate concentration, and layer thickness. Four algorithms including neural networks (an algorithm inspired by neurons in the biological brain), K-nearest neighbours (a nonlinear algorithm working by averaging the output of k neighbours), ridge regression (a continuous shrinkage algorithm that improves accuracy by adding a penalized term), and random forest (a tree-based algorithm that builds a forest of uncorrelated regression trees) were combined to achieve an accurate model.

5. Conclusions and Future Work

Extrusion bioprinting has been widely employed to create cell-incorporated constructs for tissue engineering, and to this end, printability and cell viability are two critical issues that need to be addressed. The difference between printed constructs and designed ones represents a big challenge, limiting the progress to mimic native tissue organs for tissue engineering. Our review illustrated that varying characterizations of printability were presented in the literature and that many parameters that can affect the printability of constructs mainly include those related to bioink properties, printing process parameters, and construct design. The main advantage of extrusion bioprinting compared with other technologies rests in its ability to incorporate cells into the biomaterials for printing constructs, while the process-induced forces can cause damage to the incorporated cells (or cell viability)—another unneglectable issue in bioprinting. Extensional stress and shear stress are two major process-induced forces responsible for cell damage. Some parameters, such as needle type and size, bioink concentration, and dispensing pressure, play key roles in causing cell damage. With many promising investigations on printability and cell viability, this field is still in its early stage and rigorously determining the effective parameters remains challenging for future development. Determination or optimization process based on trial and error is expensive, difficult, time-consuming, and sometimes impossible; therefore, computational methods demonstrate themselves as powerful tools. To optimize the bioprinting process, many parameters are involved in an interdependent manner. Nowadays, machine learning, as a newfound technology, represents a new horizon in the field of 3D bioprinting. The combination of ML and bioprinting can accelerate the development of bioprinting and thus tissue engineering. Currently, the main challenge to moving forward with ML in bioprinting is the limited available data. As such, we urge that it is time to establish a worldwide data-sharing network in the field of bioprinting. Also, we note that because of different settings in terms of brands of bioprinters and software around the world, sharing data represents many issues to be addressed and that standardized data of each printer by using similar open-source software for all printers could be promising. It is envisioned that ML, though relatively new in the field of bioprinting, will revolutionize bioprinting and thus tissue engineering in the future.

References 155

  1. 1.

    Abouna G.M. Organ Shortage Crisis: Problems and Possible Solutions. Transplant. Proc. 2008;40:34-38.

    Not in our library10.1016/j.transproceed.2007.11.067

  2. 2.

    Mandrycky C., Wang Z., Kim K., Kim D.H. 3D bioprinting for engineering complex tissues. Biotechnol. Adv. 2016;34:422-434.

    Not in our library10.1016/j.biotechadv.2015.12.011

  3. 3.

    Khademhosseini A., Langer R., Borenstein J., Vacanti J.P. Microscale technologies for tissue engineering and biology. Proc. Natl. Acad. Sci. USA. 2006;103:2480-2487.

    Not in our library10.1073/pnas.0507681102

  4. 4.

    Chen X.B. Extrusion Bioprinting of Scaffolds for Tissue Engineering. 2019.

    Not in our library

  5. 5.

    Kozior T., Bochnia J., Gogolewski D., Zmarzły P., Rudnik M., Szot W., Szczygieł P., Musiałek M. Analysis of Metrological Quality and Mechanical Properties of Models Manufactured with Photo-Curing PolyJet Matrix Technology for Medical Applications. Polymers. 2022;14:408.

    Not in our library10.3390/polym14030408

  6. 6.

    Betancourt N., Chen X. Review of extrusion-based multi-material bioprinting processes. Bioprinting. 2022;25:e00189.

    Not in our library10.1016/j.bprint.2021.e00189

  7. 7.

    You F., Wu X., Kelly M., Chen X. Bioprinting and in vitro characterization of alginate dialdehyde–Gelatin hydrogel bio-ink. Bio-Des. Manuf. 2020;3:48-59.

    Not in our library10.1007/s42242-020-00058-8

  8. 8.

    Delkash Y., Gouin M., Rimbeault T., Mohabatpour F., Papagerakis P., Maw S., Chen X. Bioprinting and in vitro characterization of an eggwhite-based cell-laden patch for endothelialized tissue engineering applications. J. Funct. Biomater. 2021;12:45.

    Not in our library10.3390/jfb12030045

  9. 9.

    Sadeghianmaryan A., Naghieh S., Alizadeh Sardroud H., Yazdanpanah Z., Afzal Soltani Y., Sernaglia J., Chen X. Extrusion-based printing of chitosan scaffolds and their in vitro characterization for cartilage tissue engineering. Int. J. Biol. Macromol. 2020;164:3179-3192.

    Not in our library10.1016/j.ijbiomac.2020.08.180

  10. 10.

    Ning L., Zhu N., Smith A., Rajaram A., Hou H., Srinivasan S., Mohabatpour F., He L., McLnnes A., Serpooshan V., et al. Noninvasive Three-Dimensional in Situ and In Vivo Characterization of Bioprinted Hydrogel Scaffolds Using the X-ray Propagation-Based Imaging Technique. ACS Appl. Mater. Interfaces. 2021;13:25611-25623.

    Not in our library10.1021/acsami.1c02297

  11. 11.

    Naghieh S., Sarker M.D., Sharma N.K., Barhoumi Z., Chen X. Printability of 3D printed hydrogel scaffolds: Influence of hydrogel composition and printing parameters. Appl. Sci. 2020;10:292.

    Not in our library10.3390/app10010292

  12. 12.

    Zimmerling A., Yazdanpanah Z., Cooper D.M.L., Johnston J.D., Chen X. 3D printing PCL/nHA bone scaffolds: Exploring the influence of material synthesis techniques. Biomater. Res. 2021;25:3.

    Not in our library10.1186/s40824-021-00204-y

  13. 13.

    Suntornnond R., Tan E.Y.S., An J., Chua C.K. A Mathematical Model on the Resolution of Extrusion Bioprinting for the Development of New Bioinks. Materials. 2016;9:756.

    Not in our library10.3390/ma9090756

  14. 14.

    Zhang Z., Jin Y., Yin J., Xu C., Xiong R., Christensen K., Ringeisen B.R., Chrisey D.B., Huang Y. Evaluation of bioink printability for bioprinting applications. Appl. Phys. Rev. 2018;5:041304.

    Not in our library10.1063/1.5053979

  15. 15.

    Müller M., Becher J., Schnabelrauch M., Zenobi-Wong M. Nanostructured Pluronic hydrogels as bioinks for 3D bioprinting. Biofabrication. 2015;7:035006.

    Not in our library10.1088/1758-5090/7/3/035006

  16. 16.

    Kyle S., Jessop Z.M., Al-Sabah A., Whitaker I.S. ‘Printability’ of Candidate Biomaterials for Extrusion Based 3D Printing: State-of-the-Art. Adv. Healthc. Mater. 2017;6:1700264.

    Not in our library10.1002/adhm.201700264

  17. 17.

    Zhao Y., Li Y., Mao S. Effect of bioink properties on printability and cell viability for 3D bioplotting of embryonic stem cells. Biofabrication. 2016;8:035020.

    Not in our library10.1088/1758-5090/8/3/035020

  18. 18.

    Paxton N., Smolan W., Böck T., Melchels F., Groll J., Jungst T. Proposal to assess printability of bioinks for extrusion-based bioprinting and evaluation of rheological properties governing bioprintability. Biofabrication. 2017;9:044107.

    Not in our library10.1088/1758-5090/aa8dd8

  19. 19.

    Soltan N., Ning L., Mohabatpour F., Papagerakis P., Chen X. Printability and cell viability in bioprinting alginate dialdehyde-gelatin scaffolds. ACS Biomater. Sci. Eng. 2019;5:2976-2987.

    Not in our library10.1021/acsbiomaterials.9b00167

  20. 20.

    Sarker M.D., Naghieh S., McInnes A.D., Ning L., Schreyer D.J., Chen X. Bio-fabrication of peptide-modified alginate scaffolds: Printability, mechanical stability and neurite outgrowth assessments. Bioprinting. 2019;14:e00045.

    Not in our library10.1016/j.bprint.2019.e00045

  21. 21.

    Naghieh S., Chen X. Printability–A key issue in extrusion-based bioprinting. J. Pharm. Anal. 2021;11:564-579.

    Not in our library10.1016/j.jpha.2021.02.001

  22. 22.

    Hospodiuk M., Dey M., Sosnoski D., Ozbolat I.T. The bioink: A comprehensive review on bioprintable materials. Biotechnol. Adv. 2017;35:217-239.

    Not in our library10.1016/j.biotechadv.2016.12.006

  23. 23.

    Duan B., Kapetanovic E., Hockaday L.A., Butcher J.T. 3D Printed Trileaflet Valve Conduits Using Biological Hydrogels and Human Valve Interstitial Cells. Acta Biomater. 2014;10:1836-1846.

    Not in our library10.1016/j.actbio.2013.12.005

  24. 24.

    Zhao Y., Li Y., Mao S., Sun W., Yao R. The influence of printing parameters on cell survival rate and printability in microextrusion-based 3D cell printing technology. Biofabrication. 2015;7:045002.

    Not in our library10.1088/1758-5090/7/4/045002

  25. 25.

    Hou X., Chen G., Xing T., Wei Z. Reactive ink formulated with various alcohols for improved properties and printing quality onto cotton fabrics. J. Eng. Fibers Fabr. 2019;14:155892501984924.

    Not in our library10.1177/1558925019849242

  26. 26.

    Atala A., Yoo M., Yoo J.J., Atala A., James J.Y. Essentials of 3D Biofabrication and Translation. 2015.

    Not in our library

  27. 27.

    Chimene D., Lennox K.K., Kaunas R.R., Gaharwar A.K. Advanced Bioinks for 3D Printing: A Materials Science Perspective. Ann. Biomed. Eng. 2016;44:2090-2102.

    Not in our library10.1007/s10439-016-1638-y

  28. 28.

    Chen X.B., Ke H. Effects of fluid properties on dispensing processes for electronics packaging. IEEE Trans. Electron. Packag. Manuf. 2006;29:75-82.

    Not in our library10.1109/tepm.2006.874964

  29. 29.

    Fu Z., Naghieh S., Xu C., Wang C., Sun W., Chen X. Printability in extrusion bioprinting. Biofabrication. 2021;13:033001.

    Not in our library10.1088/1758-5090/abe7ab

  30. 30.

    Liu W., Zhang Y.S., Heinrich M.A., De Ferrari F., Jang H.L., Bakht S.M., Alvarez M.M., Yang J., Li Y.C., Trujillo-de Santiago G., et al. Rapid Continuous Multimaterial Extrusion Bioprinting. Adv. Mater. 2017;29:1604630.

    Not in our library10.1002/adma.201604630

  31. 31.

    Lee J.M., Ng W.L., Yeong W.Y. Resolution and shape in bioprinting: Strategizing towards complex tissue and organ printing. Appl. Phys. Rev. 2019;6:011307.

    Not in our library10.1063/1.5053909

  32. 32.

    Chen X.B., Li M.G., Ke H. Modeling of the flow rate in the dispensing-based process for fabricating tissue scaffolds. J. Manuf. Sci. Eng. Trans. ASME. 2008;130:021003.

    Not in our library10.1115/1.2789725

  33. 33.

    Li M.G., Tian X.Y., Chen X.B. Modeling of flow rate, pore size, and porosity for the dispensing-based tissue scaffolds fabrication. J. Manuf. Sci. Eng. Trans. ASME. 2009;131:034501.

    Not in our library10.1115/1.3123331

  34. 34.

    Sarker M., Chen X.B. Modeling the Flow Behavior and Flow Rate of Medium Viscosity Alginate for Scaffold Fabrication with a Three-Dimensional Bioplotter. J. Manuf. Sci. Eng. Trans. ASME. 2017;139:081002.

    Not in our library10.1115/1.4036226

  35. 35.

    Chang C.C., Boland E.D., Williams S.K., Hoying J.B. Direct-write bioprinting three-dimensional biohybrid systems for future regenerative therapies. J. Biomed. Mater. Res.-Part B Appl. Biomater. 2011;98B:160-170.

    Not in our library10.1002/jbm.b.31831

  36. 36.

    Billiet T., Gevaert E., De Schryver T., Cornelissen M., Dubruel P. The 3D printing of gelatin methacrylamide cell-laden tissue-engineered constructs with high cell viability. Biomaterials. 2014;35:49-62.

    Not in our library10.1016/j.biomaterials.2013.09.078

  37. 37.

    Naghieh S., Karamooz-Ravari M.R., Sarker M.D., Karki E., Chen X. Influence of crosslinking on the mechanical behavior of 3D printed alginate scaffolds: Experimental and numerical approaches. J. Mech. Behav. Biomed. Mater. 2018;80:111-118.

    Not in our library10.1016/j.jmbbm.2018.01.034

  38. 38.

    Sarker M., Izadifar M., Schreyer D., Chen X. Influence of ionic crosslinkers (Ca2+ /Ba2+ /Zn2+) on the mechanical and biological properties of 3D Bioplotted Hydrogel Scaffolds. J. Biomater. Sci. Polym. Ed. 2018;29:1126-1154.

    Not in our library10.1080/09205063.2018.1433420

  39. 39.

    Lee J.M., Yeong W.Y. Design and Printing Strategies in 3D Bioprinting of Cell-Hydrogels: A Review. Adv. Healthc. Mater. 2016;5:2856-2865.

    Not in our library10.1002/adhm.201600435

  40. 40.

    Kesti M., Eberhardt C., Pagliccia G., Kenkel D., Grande D., Boss A., Zenobi-Wong M. Bioprinting Complex Cartilaginous Structures with Clinically Compliant Biomaterials. Adv. Funct. Mater. 2015;25:7406-7417.

    Not in our library10.1002/adfm.201503423

  41. 41.

    Dang Q., Liu K., Zhang Z., Liu C., Liu X., Xin Y., Cheng X., Xu T., Cha D., Fan B. Fabrication and evaluation of thermosensitive chitosan/collagen/α, β-glycerophosphate hydrogels for tissue regeneration. Carbohydr. Polym. 2017;167:145-157.

    Not in our library10.1016/j.carbpol.2017.03.053

  42. 42.

    Wüst S., Godla M.E., Müller R., Hofmann S. Tunable hydrogel composite with two-step processing in combination with innovative hardware upgrade for cell-based three-dimensional bioprinting. Acta Biomater. 2014;10:630-640.

    Not in our library10.1016/j.actbio.2013.10.016

  43. 43.

    He Y., Tuck C.J., Prina E., Kilsby S., Christie S.D.R., Edmondson S., Hague R.J.M., Rose F.R.A.J., Wildman R.D. A new photocrosslinkable polycaprolactone-based ink for three-dimensional inkjet printing. J. Biomed. Mater. Res.-Part B Appl. Biomater. 2017;105:1645-1657.

    Not in our library10.1002/jbm.b.33699

  44. 44.
  45. 45.
  46. 46.

    Kim Y., Kang K., Jeong J., Paik S.S., Kim J.S., Park S.A., Kim W.D., Park J., Choi D. Three-dimensional (3D) printing of mouse primary hepatocytes to generate 3D hepatic structure. Ann. Surg. Treat. Res. 2017;92:67-72.

    Not in our library10.4174/astr.2017.92.2.67

  47. 47.

    Naghieh S., Sarker M.D., Abelseth E., Chen X. Indirect 3D bioprinting and characterization of alginate scaffolds for potential nerve tissue engineering applications. J. Mech. Behav. Biomed. Mater. 2019;93:183-193.

    Not in our library10.1016/j.jmbbm.2019.02.014

  48. 48.

    Markstedt K., Mantas A., Tournier I., Ha D., Gatenholm P. 3D Bioprinting Human Chondrocytes with Nanocellulose−Alginate Bioink for Cartilage Tissue Engineering Applications. Biomacromolecules. 2015;16:1489-1496.

    Not in our library10.1021/acs.biomac.5b00188

  49. 49.

    Fu Z., Ouyang L., Xu R., Yang Y., Sun W. Responsive biomaterials for 3D bioprinting: A review. Mater. Today. 2022;52:112-132.

    Not in our library10.1016/j.mattod.2022.01.001

  50. 50.

    López-Marcial G.R., Zeng A.Y., Osuna C., Dennis J., García J.M., O’Connell G.D. Agarose-Based Hydrogels as Suitable Bioprinting Materials for Tissue Engineering. ACS Biomater. Sci. Eng. 2018;4:3610-3616.

    Not in our library10.1021/acsbiomaterials.8b00903

  51. 51.

    Lee K.Y., Mooney D.J. Hydrogels for Tissue Engineering. Chem. Rev. 2001;101:1869-1880.

    Not in our library10.1021/cr000108x

  52. 52.

    Gong C., Kong Z., Wang X. The effect of agarose on 3d bioprinting. Polymers. 2021;13:4028.

    Not in our library10.3390/polym13224028

  53. 53.

    Nadernezhad A., Caliskan O.S., Topuz F., Afghah F., Erman B., Koc B. Nanocomposite Bioinks Based on Agarose and 2D Nanosilicates with Tunable Flow Properties and Bioactivity for 3D Bioprinting. ACS Appl. Bio. Mater. 2019;2:796-806.

    Not in our library10.1021/acsabm.8b00665

  54. 54.

    Tako M., Nakamura S. Gelation mechanism of agarose. Carbohydr. Res. 1988;180:277-284.

    Not in our library10.1016/0008-6215(88)80084-3

  55. 55.
  56. 56.

    Du J., Dai H., Wang H., Yu Y., Zhu H., Fu Y., Ma L., Peng L., Li L., Wang Q., et al. Preparation of high thermal stability gelatin emulsion and its application in 3D printing. Food Hydrocoll. 2021;113:106536.

    Not in our library10.1016/j.foodhyd.2020.106536

  57. 57.
  58. 58.
  59. 59.

    Rajabi M., McConnell M., Cabral J., Ali M.A. Chitosan hydrogels in 3D printing for biomedical applications. Carbohydr. Polym. 2021;260:117768.

    Not in our library10.1016/j.carbpol.2021.117768

  60. 60.

    Wu Q., Therriault D., Heuzey M.-C. Processing and Properties of Chitosan Inks for 3D Printing of Hydrogel Microstructures. ACS Biomater. Sci. Eng. 2018;4:2643-2652.

    Not in our library10.1021/acsbiomaterials.8b00415

  61. 61.

    Wu Q., Maire M., Lerouge S., Therriault D., Heuzey M.-C. 3D Printing of Microstructured and Stretchable Chitosan Hydrogel for Guided Cell Growth. Adv. Biosyst. 2017;1:1700058.

    Not in our library10.1002/adbi.201700058

  62. 62.

    Lee V., Singh G., Trasatti J.P., Bjornsson C., Xu X., Tran T.N., Yoo S.S., Dai G., Karande P. Design and fabrication of human skin by three-dimensional bioprinting. Tissue Eng.-Part C Methods. 2014;20:473-484.

    Not in our library10.1089/ten.tec.2013.0335

  63. 63.

    Fu F., Qin Z., Xu C., Chen X.Y., Li R.X., Wang L.N., Peng D.W., Sun H.T., Tu Y., Chen C., et al. Magnetic resonance imaging-three-dimensional printing technology fabricates customized scaffolds for brain tissue engineering. Neural Regen. Res. 2017;12:614-622.

    Not in our library10.4103/1673-5374.205101

  64. 64.

    Rhee S., Puetzer J.L., Mason B.N., Reinhart-King C.A., Bonassar L.J. 3D Bioprinting of Spatially Heterogeneous Collagen Constructs for Cartilage Tissue Engineering. ACS Biomater. Sci. Eng. 2016;2:1800-1805.

    Not in our library10.1021/acsbiomaterials.6b00288

  65. 65.

    Abelseth E., Abelseth L., De La Vega L., Beyer S.T., Wadsworth S.J., Willerth S.M. 3D Printing of Neural Tissues Derived from Human Induced Pluripotent Stem Cells Using a Fibrin-Based Bioink. ACS Biomater. Sci. Eng. 2019;5:234-243.

    Not in our library10.1021/acsbiomaterials.8b01235

  66. 66.

    England S., Rajaram A., Schreyer D.J., Chen X. Bioprinted fibrin-factor XIII-hyaluronate hydrogel scaffolds with encapsulated Schwann cells and their in vitro characterization for use in nerve regeneration. Bioprinting. 2017;5:1-9.

    Not in our library10.1016/j.bprint.2016.12.001

  67. 67.

    Zhao D., Huang Y., Ao Y., Han C., Wang Q., Li Y., Liu J., Wei Q., Zhang Z. Effect of pore geometry on the fatigue properties and cell affinity of porous titanium scaffolds fabricated by selective laser melting. J. Mech. Behav. Biomed. Mater. 2018;88:478-487.

    Not in our library10.1016/j.jmbbm.2018.08.048

  68. 68.

    Li H., Yin Y., Xiang Y., Liu H., Guo R. A novel 3D printing PCL/GelMA scaffold containing USPIO for MRI-guided bile duct repair. Biomed. Mater. 2020;15:45004.

    Not in our library10.1088/1748-605x/ab797a

  69. 69.

    Ouyang L., Highley C.B., Rodell C.B., Sun W., Burdick J.A. 3D Printing of Shear-Thinning Hyaluronic Acid Hydrogels with Secondary Cross-Linking. ACS Biomater. Sci. Eng. 2016;2:1743-1751.

    Not in our library10.1021/acsbiomaterials.6b00158

  70. 70.

    Highley C.B., Rodell C.B., Burdick J.A. Direct 3D Printing of Shear-Thinning Hydrogels into Self-Healing Hydrogels. Adv. Mater. 2015;27:5075-5079.

    Not in our library10.1002/adma.201501234

  71. 71.

    Petta D., D’Amora U., Ambrosio L., Grijpma D.W., Eglin D., D’Este M. Hyaluronic acid as a bioink for extrusion-based 3D printing. Biofabrication. 2020;12:032001.

    Not in our library10.1088/1758-5090/ab8752

  72. 72.

    Shie M.Y., Chang W.C., Wei L.J., Huang Y.H., Chen C.H., Shih C.T., Chen Y.W., Shen Y.F. 3D printing of cytocompatible water-based light-cured polyurethane with hyaluronic acid for cartilage tissue engineering applications. Materials. 2017;10:136.

    Not in our library10.3390/ma10020136

  73. 73.

    Ouyang L., Highley C.B., Sun W., Burdick J.A. A Generalizable Strategy for the 3D Bioprinting of Hydrogels from Nonviscous Photo-crosslinkable Inks. Adv. Mater. 2017;29:1604983.

    Not in our library10.1002/adma.201604983

  74. 74.
  75. 75.

    Bai J., Wang H., Gao W., Liang F., Wang Z., Zhou Y., Lan X., Chen X., Cai N., Huang W., et al. Melt electrohydrodynamic 3D printed poly (ε-caprolactone)/polyethylene glycol/roxithromycin scaffold as a potential anti-infective implant in bone repair. Int. J. Pharm. 2020;576:118941.

    Not in our library10.1016/j.ijpharm.2019.118941

  76. 76.

    Khan F., Valere S., Fuhrmann S., Arrighi V., Bradley M. Synthesis and cellular compatibility of multi-block biodegradable poly(ε-caprolactone)-based polyurethanes. J. Mater. Chem. B. 2013;1:2590-2600.

    Not in our library10.1039/c3tb00358b

  77. 77.

    Hsiao S.H., Hsu S.H. Synthesis and Characterization of Dual Stimuli-Sensitive Biodegradable Polyurethane Soft Hydrogels for 3D Cell-Laden Bioprinting. ACS Appl. Mater. Interfaces. 2018;10:29273-29287.

    Not in our library10.1021/acsami.8b08362

  78. 78.

    Hung K.C., Tseng C.S., Hsu S.H. Synthesis and 3D Printing of biodegradable polyurethane elastomer by a water-based process for cartilage tissue engineering applications. Adv. Healthc. Mater. 2014;3:1578-1587.

    Not in our library10.1002/adhm.201400018

  79. 79.

    Domínguez-Robles J., Mancinelli C., Mancuso E., García-Romero I., Gilmore B.F., Casettari L., Larrañeta E., Lamprou D.A. 3D printing of drug-loaded thermoplastic polyurethane meshes: A potential material for soft tissue reinforcement in vaginal surgery. Pharmaceutics. 2020;12:63.

    Not in our library10.3390/pharmaceutics12010063

  80. 80.

    Murphy S.V., Skardal A., Atala A. Evaluation of hydrogels for bio-printing applications. J. Biomed. Mater. Res.-Part A. 2013;101A:272-284.

    Not in our library10.1002/jbm.a.34326

  81. 81.

    Rajaram A., Schreyer D.J., Chen D.X.B. Use of the polycation polyethyleneimine to improve the physical properties of alginate-hyaluronic acid hydrogel during fabrication of tissue repair scaffolds. J. Biomater. Sci. Polym. Ed. 2015;26:433-445.

    Not in our library10.1080/09205063.2015.1016383

  82. 82.
  83. 83.

    Chung J.H.Y., Naficy S., Yue Z., Kapsa R., Quigley A., Moulton S.E., Wallace G.G. Bio-ink properties and printability for extrusion printing living cells. Biomater. Sci. 2013;1:763-773.

    Not in our library10.1039/c3bm00012e

  84. 84.

    Mouser V.H.M., Melchels F.P.W., Visser J., Dhert W.J.A., Gawlitta D., Malda J. Yield stress determines bioprintability of hydrogels based on gelatin-methacryloyl and gellan gum for cartilage bioprinting. Biofabrication. 2016;8:35003.

    Not in our library10.1088/1758-5090/8/3/035003

  85. 85.

    Bertassoni L.E., Cardoso J.C., Manoharan V., Cristino A.L., Bhise N.S., Araujo W.A., Zorlutuna P., Vrana N.E., Ghaemmaghami A.M., Dokmeci M.R., et al. Direct-write bioprinting of cell-laden methacrylated gelatin hydrogels. Biofabrication. 2014;6:024105.

    Not in our library10.1088/1758-5082/6/2/024105

  86. 86.

    Liu W., Heinrich M.A., Zhou Y., Akpek A., Hu N., Liu X., Guan X., Zhong Z., Jin X., Khademhosseini A., et al. Extrusion Bioprinting of Shear-Thinning Gelatin Methacryloyl Bioinks. Adv. Healthc. Mater. 2017;6:1601451.

    Not in our library10.1002/adhm.201601451

  87. 87.

    Izadifar Z., Chang T., Kulyk W., Chen X., Eames B.F. Analyzing biological performance of 3D-printed, cell-impregnated hybrid constructs for cartilage tissue engineering. Tissue Eng.-Part C Methods. 2016;22:173-188.

    Not in our library10.1089/ten.tec.2015.0307

  88. 88.

    Olubamiji A.D., Zhu N., Chang T., Nwankwo C.K., Izadifar Z., Honaramooz A., Chen X., Eames B.F. Traditional Invasive and Synchrotron-Based Noninvasive Assessments of Three-Dimensional-Printed Hybrid Cartilage Constructs in Situ. Tissue Eng.-Part C Methods. 2017;23:156-168.

    Not in our library10.1089/ten.tec.2016.0368

  89. 89.

    Kundu J., Shim J.-H., Jang J., Kim S.-W., Cho D.-W. An additive manufacturing-based PCL–alginate–chondrocyte bioprinted scaffold for cartilage tissue engineering. J. Tissue Eng. Regen. Med. 2015;9:1286-1297.

    Not in our library10.1002/term.1682

  90. 90.

    Pati F., Shim J.-H., Lee J.-S., Cho D.-W. 3D printing of cell-laden constructs for heterogeneous tissue regeneration. Manuf. Lett. 2013;1:49-53.

    Not in our library10.1016/j.mfglet.2013.09.004

  91. 91.

    Lee J.-S., Hong J.M., Jung J.W., Shim J.-H., Oh J.-H., Cho D.-W. 3D printing of composite tissue with complex shape applied to ear regeneration. Biofabrication. 2014;6:024103.

    Not in our library10.1088/1758-5082/6/2/024103

  92. 92.

    Hinton T.J., Hudson A., Pusch K., Lee A., Feinberg A.W. 3D Printing PDMS Elastomer in a Hydrophilic Support Bath via Freeform Reversible Embedding. 3D Printers. 2016;2:1781-1786.

    Not in our library10.1021/acsbiomaterials.6b00170

  93. 93.

    Ding H., Chang R.C. Printability Study of Bioprinted Tubular Structures Using Liquid Hydrogel Precursors in a Support Bath. Appl. Sci. 2018;8:403.

    Not in our library10.3390/app8030403

  94. 94.

    Sodupe-Ortega E., Sanz-Garcia A., Pernia-Espinoza A., Escobedo-Lucea C. Accurate Calibration in Multi-Material 3D Bioprinting for Tissue Engineering. Materials. 2018;11:1402.

    Not in our library10.3390/ma11081402

  95. 95.

    Wong K.H.K., Chan J.M., Kamm R.D., Tien J. Microfluidic Models of Vascular Functions. Annu. Rev. Biomed. Eng. 2012;14:205-230.

    Not in our library10.1146/annurev-bioeng-071811-150052

  96. 96.

    Potter C.M.F., Lao K.H., Zeng L., Xu Q. Role of Biomechanical Forces in Stem Cell Vascular Lineage Differentiation. Arterioscler. Thromb. Vasc. Biol. 2014;34:2184-2190.

    Not in our library10.1161/atvbaha.114.303423

  97. 97.

    Boularaoui S., Al Hussein G., Khan K.A., Christoforou N., Stefanini C. An overview of extrusion-based bioprinting with a focus on induced shear stress and its effect on cell viability. Bioprinting. 2020;20:e00093.

    Not in our library10.1016/j.bprint.2020.e00093

  98. 98.

    Rajaram A., Schreyer D., Chen D. Bioplotting Alginate/Hyaluronic Acid Hydrogel Scaffolds with Structural Integrity and Preserved Schwann Cell Viability. 3D Print. Addit. Manuf. 2014;1:194-203.

    Not in our library10.1089/3dp.2014.0006

  99. 99.

    Ning L., Xu Y., Chen X., Schreyer D.J. Influence of mechanical properties of alginate-based substrates on the performance of Schwann cells in culture. J. Biomater. Sci. Polym. Ed. 2016;27:898-915.

    Not in our library10.1080/09205063.2016.1170415

  100. 100.

    Ning L., Guillemot A., Zhao J., Kipouros G., Chen X. Influence of Flow Behavior of Alginate-Cell Suspensions on Cell Viability and Proliferation. Tissue Eng. Part C Methods. 2016;22:652-662.

    Not in our library10.1089/ten.tec.2016.0011

  101. 101.

    Li M., Tian X., Kozinski J.A., Chen X., Hwang D.K. Modeling Mechanical Cell Damage in the Bioprinting Process Employing a Conical Needle. J. Mech. Med. Biol. 2015;15:1550073.

    Not in our library10.1142/s0219519415500736

  102. 102.

    Ning L., Yang B., Mohabatpour F., Betancourt N., Sarker M.D., Papagerakis P., Chen X. Process-induced cell damage: Pneumatic versus screw-driven bioprinting. Biofabrication. 2020;12:025011.

    Not in our library10.1088/1758-5090/ab5f53

  103. 103.

    Blaeser A., Filipa D., Campos D., Puster U., Richtering W., Stevens M.M. Controlling Shear Stress in 3D Bioprinting is a Key Factor to Balance Printing Resolution and Stem Cell Integrity. Adv. Healthc. Mater. 2016;5:326-333.

    Not in our library10.1002/adhm.201500677

  104. 104.

    Hull S.M., Brunel L.G., Heilshorn S.C. 3D Bioprinting of Cell-Laden Hydrogels for Improved Biological Functionality. Adv. Mater. 2022;34:2103691.

    Not in our library10.1002/adma.202103691

  105. 105.

    Nair K., Gandhi M., Khalil S., Yan K.C., Marcolongo M., Barbee K., Sun W. Characterization of cell viability during bioprinting processes. Biotechnol. J. 2009;4:1168-1177.

    Not in our library10.1002/biot.200900004

  106. 106.

    Li M., Tian X., Schreyer D.J., Chen X. Effect of needle geometry on flow rate and cell damage in the dispensing-based biofabrication process. Biotechnol. Prog. 2011;27:1777-1784.

    Not in our library10.1002/btpr.679

  107. 107.

    Lucas L., Aravind A., Emma P., Christophe M., Edwin-Joffrey C. Rheology, simulation and data analysis toward bioprinting cell viability awareness. Bioprinting. 2021;21:e00119.

    Not in our library10.1016/j.bprint.2020.e00119

  108. 108.

    Kingsley D.M., Ouyang L., Yao R., Mao S., Chen X., Na J., Sun W. Three-dimensional bioprinting of embryonic stem cells directs highly uniform embryoid body formation Three-dimensional bioprinting of embryonic stem cells directs highly uniform embryoid body formation. Biofabrication. 2015;7:044101.

    Not in our library10.1088/1758-5090/7/4/044101

  109. 109.

    Murphy S.V., Atala A. 3D bioprinting of tissues and organs. Nat. Biotechnol. 2014;32:773-785.

    Not in our library10.1038/nbt.2958

  110. 110.

    Baena J.M., Jiménez G., López-Ruiz E., Antich C., Griñán-Lisón C., Perán M., Gálvez-Martín P., Marchal J.A. Volume-by-volume bioprinting of chondrocytes-alginate bioinks in high temperature thermoplastic scaffolds for cartilage regeneration. Exp. Biol. Med. 2019;244:13-21.

    Not in our library10.1177/1535370218821128

  111. 111.

    Mohd Bohari S.P., Hukins D., Grover L. Effect of calcium alginate concentration on viability and proliferation of encapsulated fibroblasts. Biomed. Mater. Eng. 2011;21:159-170.

    Not in our library10.3233/bme-2011-0665

  112. 112.

    Li M., Tian X., Zhu N., Schreyer D.J., Chen X. Modeling process-induced cell damage in the biodispensing process. Tissue Eng. Part C Methods. 2010;16:533-542.

    Not in our library10.1089/ten.tec.2009.0178

  113. 113.

    Ning L., Betancourt N., Schreyer D.J., Chen X. Characterization of Cell Damage and Proliferative Ability during and after Bioprinting. ACS Biomater. Sci. Eng. 2018;4:3906-3918.

    Not in our library10.1021/acsbiomaterials.8b00714

  114. 114.

    Göhl J., Markstedt K., Mark A., Håkansson K., Gatenholm P., Edelvik F. Simulations of 3D bioprinting: Predicting bioprintability of nanofibrillar inks. Biofabrication. 2018;10:34105.

    Not in our library10.1088/1758-5090/aac872

  115. 115.

    Stiehm M., Wüstenhagen C., Siewert S., Grabow N., Schmitz K.-P. Numerical simulation of pulsatile flow through a coronary nozzle model based on FDA’s benchmark geometry. Curr. Dir. Biomed. Eng. 2017;3:775-778.

    Not in our library10.1515/cdbme-2017-0163

  116. 116.

    Brindha J., Privita Edwina R.A.G., Rajesh P.K., Rani P. Influence of rheological properties of protein bio-inks on printability: A simulation and validation study. Mater. Today Proc. 2016;3:3285-3295.

    Not in our library10.1016/j.matpr.2016.10.010

  117. 117.

    Wu H.-C., Lin H.-J. Effects of Actuating Pressure Waveforms on the Droplet Behavior in a Piezoelectric Inkjet. Mater. Trans. 2010;51:2269-2276.

    Not in our library10.2320/matertrans.m2010123

  118. 118.

    Leppiniemi J., Lahtinen P., Paajanen A., Mahlberg R., Metsä-Kortelainen S., Pinomaa T., Pajari H., Vikholm-Lundin I., Pursula P., Hytönen V.P. 3D-Printable Bioactivated Nanocellulose-Alginate Hydrogels. ACS Appl. Mater. Interfaces. 2017;9:21959-21970.

    Not in our library10.1021/acsami.7b02756

  119. 119.

    Brackbill J.U., Kothe D.B., Zemach C. A continuum Method for Modeling Surface Tension. Comput. Phys. 1992;100:335-354.

    Not in our library10.1016/0021-9991(92)90240-y

  120. 120.

    Furlani E.P. Fluid Mechanics for Inkjet Printing. Fundamentals of Inkjet Printing. 2015;13-56.

    Not in our library

  121. 121.

    Caboussat A. Numerical Simulation of Two-Phase Free Surface Flows. Arch. Comput. Methods Eng. 2005;12:165-224.

    Not in our library10.1007/bf03044518

  122. 122.

    Yeoh G.H., Tu J., Yeoh G.H., Tu J. Chapter 3-Solution Methods for Multi-Phase Flows. Computational Techniques for Multiphase Flows. 2010;95-242.

    Not in our library

  123. 123.

    Chan K.S., Pericleous K., Cross M. Numerical simulation of flows encountered during mold-filling. Top. Catal. 1991;15:624-631.

    Not in our library10.1016/s0307-904x(09)81008-1

  124. 124.

    Kothe D.B. Volume Tracking of Interfaces Having Surface The University of Memphis. 1999;859.

    Not in our library10.2514/6.1996-859

  125. 125.

    Noh W.F., Woodward P. SLIC (Simple Line Interface Calculation). 1976.

    Not in our library

  126. 126.

    Youngs D. Time-Dependent Multi-material Flow with Large Fluid Distortion. Numer. Methods Fluid Dyn. 1982;273-285.

    Not in our library

  127. 127.

    Lee M.S., Aute V., Riaz A., Radermacher R. A Review on Direct Two-Phase, Phase Change Flow Simulation Methods and their Applications. Proceedings of the International Refrigeration and Air Conditioning Conference. 1-9.

    Not in our library

  128. 128.

    Shepel S.V., Smith B.L. On surface tension modelling using the level set method. Numer. Methods Fluids. 2009;59:147-171.

    Not in our library10.1002/fld.1804

  129. 129.

    Hutchings I.M., Martin G.D., Hoath S.D. Introductory Remarks. Fundamentals of Inkjet Printing. 2015;1-12.

    Not in our library

  130. 130.

    Landau L.D., Lifshitz E.M., Landau L.D., Lifshitz E.M. Chapter VII-Surface Phenomena. Fluid Mechanics (Second Edition). 1987;238-250.

    Not in our library

  131. 131.

    Shirani E., Ashgriz N., Mostaghimi J. Interface pressure calculation based on conservation of momentum for front capturing methods. J. Comput. Phys. 2005;203:154-175.

    Not in our library10.1016/j.jcp.2004.08.017

  132. 132.

    Lafaurie B., Nardoni C., Scardovelei R., Zaleski S., Zanetti G. Modeling Merging and Fragmentation in Multiphase flows with SURFER. Comput. Phys. 1994;113:147.

    Not in our library10.1006/jcph.1994.1123

  133. 133.

    Lepowsky E., Muradoglu M., Tasoglu S. Bioprinting Towards preserving post-printing cell viability and improving the resolution: Past, present, and future of 3D bioprinting theory. Bioprinting. 2018;11:e00034.

    Not in our library10.1016/j.bprint.2018.e00034

  134. 134.

    Hendriks J., Visser C.W., Henke S., Leijten J., Saris D.B.F. Optimizing cell viability in droplet- based cell deposition. Nat. Publ. Gr. 2015;5:11304.

    Not in our library10.1038/srep11304

  135. 135.

    Lee S.S., Yim Y., Ahn K.H., Lee S.J. Extensional flow-based assessment of red blood cell deformability using hyperbolic converging microchannel. Biomed. Microdevices. 2009;11:1021-1027.

    Not in our library10.1007/s10544-009-9319-3

  136. 136.

    Tanzeglock T., Soos M., Stephanopoulos G., Morbidelli M. Induction of Mammalian Cell Death by Simple Shear and Extensional Flows. Biotechnol. Bioeng. 2009;104:360-370.

    Not in our library10.1002/bit.22405

  137. 137.

    Aguado B.A., Mulyasasmita W., Su J., Lampe K.J., Heilshorn S.C. Improving Viability of Stem Cells During Syringe Needle Flow Through the Design of Hydrogel Cell Carriers. Tissue Eng. Part A. 2012;18:806-815.

    Not in our library10.1089/ten.tea.2011.0391

  138. 138.

    Reina-Romo E., Mandal S., Amorim P., Bloemen V., Ferraris E., Geris L. Towards the Experimentally-Informed In Silico Nozzle Design Optimization for Extrusion-Based Bioprinting of Shear-Thinning Hydrogels. Front. Bioeng. Biotechnol. 2021;9:701778.

    Not in our library10.3389/fbioe.2021.701778

  139. 139.

    Yu C., Jiang J. A perspective on using machine learning in 3D bioprinting. Int. J. Bioprint. 2020;6:4-11.

    Not in our library10.18063/ijb.v6i1.253

  140. 140.

    An J., Chua C.K., Mironov V. Application of Machine Learning in 3D Bioprinting: Focus on Development of Big Data and Digital Twin. Int. J. Bioprint. 2021;7:342.

    Not in our library10.18063/ijb.v7i1.342

  141. 141.

    Ng W.L., Chan A., Ong Y.S., Chua C.K. Deep learning for fabrication and maturation of 3D bioprinted tissues and organs. Virtual Phys. Prototyp. 2020;15:340-358.

    Not in our library10.1080/17452759.2020.1771741

  142. 142.

    Costa J.B., Silva-Correia J., Reis R.L., Oliveira J.M. Deep learning in bioengineering and biofabrication: A powerful technology boosting translation from research to clinics. J. 3D Print. Med. 2021;5:191-211.

    Not in our library10.2217/3dp-2021-0007

  143. 143.

    Ruberu K., Senadeera M., Rana S., Gupta S., Chung J., Yue Z., Venkatesh S., Wallace G. Coupling machine learning with 3D bioprinting to fast track optimisation of extrusion printing. Appl. Mater. Today. 2021;22:100914.

    Not in our library10.1016/j.apmt.2020.100914

  144. 144.

    Jin Z., Zhang Z., Shao X., Gu G.X. Monitoring Anomalies in 3D Bioprinting with Deep Neural Networks. ACS Biomater. Sci. Eng. 2021.

    Not in our library10.1021/acsbiomaterials.0c01761

  145. 145.

    Shi J., Song J., Song B., Lu W.F. Multi-Objective Optimization Design through Machine Learning for Drop-on-Demand Bioprinting. Engineering. 2019;5:586-593.

    Not in our library10.1016/j.eng.2018.12.009

  146. 146.

    Shi J., Wu B., Song B., Song J., Li S., Trau D., Lu W.F. Learning-Based Cell Injection Control for Precise Drop-on-Demand Cell Printing. Ann. Biomed. Eng. 2018;46:1267-1279.

    Not in our library10.1007/s10439-018-2054-2

  147. 147.

    Menon A., Póczos B., Feinberg A.W., Washburn N.R. Optimization of Silicone 3D Printing with Hierarchical Machine Learning. 3D Print. Addit. Manuf. 2019;6:181-189.

    Not in our library10.1089/3dp.2018.0088

  148. 148.

    Conev A., Litsa E.E., Perez M.R., Diba M., Mikos A.G., Kavraki L.E. Machine learning-guided three-dimensional printing of tissue engineering scaffolds. Tissue Eng.-Part A. 2020;26:1359-1368.

    Not in our library10.1089/ten.tea.2020.0191

  149. 149.

    Lee J., Oh S.J., An S.H., Kim W.D., Kim S.H., Kim S.H. Machine learning-based design strategy for 3D printable bioink: Elastic modulus and yield stress determine printability. Biofabrication. 2020;12:035018.

    Not in our library10.1088/1758-5090/ab8707

  150. 150.

    Tian S., Stevens R., McInnes B.T., Lewinski N.A. Machine assisted experimentation of extrusion-based bioprinting systems. Micromachines. 2021;12:780.

    Not in our library10.3390/mi12070780

  151. 151.

    Specht D.F. A general regression neural network. IEEE Trans. Neural Netw. 1991;2:568-576.

    Not in our library10.1109/72.97934

  152. 152.

    Imandoust S.B., Bolandraftar M. Application of K-Nearest Neighbor (KNN) Approach for Predicting Economic Events: Theoretical Background. Int. J. Eng. Res. Appl. 2013;3:605-610.

    Not in our library

  153. 153.

    Hastie T., Tibshirani R., James G., Witten D. An Introduction to Statistical Learning, Springer Texts. 2006;Volume 102.

    Not in our library

  154. 154.

    Breiman L. Random Forests. Mach. Learn. 2001;45:5-32.

    Not in our library10.1023/a:1010933404324

  155. 155.

    Xu H., Liu Q., Casillas J., Mcanally M., Mubtasim N., Gollahon L.S., Wu D., Xu C. Prediction of cell viability in dynamic optical projection stereolithography-based bioprinting using machine learning. J. Intell. Manuf. 2020;33:995-1005.

    Not in our library10.1007/s10845-020-01708-5

Reads

Read by people on this page

None yet.

Checked or read by AI through naulon

None yet.

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.

Are you an author?

Is this your paper?

Claim it to add your note and be paid when agents cite it. Free.