For the purpose of investigating the effect of Zn replacement of In₃Sn on the hydrogen production performance of Al-rich alloy ingots, Al-Ga-In₃Sn alloys with various Zn dosages (0−5 wt.%) were prepared by a traditional melting and casting technique. The phase compositions and microstructures were characterized using X-ray diffractometer (XRD) and scanning electron microscope (SEM) with an Energy Dispersed X-ray system (EDS). The SEM results indicate that, with a small amount of Zn instead of In₃Sn, the number and total area of grain boundary (GB) phases will decrease gradually, and the average single GB area will eventually stabilize. The distribution of Zn in the alloy is similar to that of Ga, and an area with high Zn content appeared in the high-Zn-doped sample. The melting behaviors of Al with other metals were measured by DSC. The reaction of these alloys and water were investigated at different temperatures. Compared with Al-Ga-In₃Sn alloy, low addition of Zn changed the composition of GB phase and increased the maximum hydrogen production rate. The reason for the changes in the hydrolysis reaction of Al with the addition of Zn was discussed.

Abstract licence: CC BY

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.