Modification and adsorption performance of ultrafine iron matrix composite powder

Ultrafine matrix composite powder was prepared from brown corundum slag, grinding balls, anhydrous ethanol, and modifier using a planetary ball mill. The adsorption material was used for dyeing wastewater treatment. A pH instrument, spectrophotometer, and digital water bath oscillator were used to study the amount of modifier, milling speed, milling time, ball-to-powder weight ratio, and slurry concentration to investigate the effects of preparation conditions on the adsorption performance of adsorbent material. The prepared adsorbents and activated carbon were used to adsorb methylene blue in solution under the same conditions to compare adsorbent dosage, adsorption time, temperature, pH of solution, and initial concentration of methylene blue and to study their effects on methylene blue decolorization rate. The experiment results show that dosage of R of 7.5%, ball-to-powder weight ratio of 14:1, rotational speed of 500 rpm, slurry concentration of 20%, and ball milling time of 2.5 h were the optimum parameters. The composite powder (4 g/l) was added to methylene blue wastewater (35 mg/l), pH was adjusted to 6, and adsorption was carried out for 0.5 h at 30°C. The removal rate reached 99.4%.

Abstract licence: CC BY

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.