Research on the Microstructure and Mechanical Property of Ti-7Cu Alloy after Semi-Solid Forging

The present work is focused on the development of microstructure of Ti-7Cu alloy as a function of forging temperature and forging ratio in semi-solid state and the influence of resulting microstructure on the mechanical properties. The experimental results showed that the dynamic recrystallization occurred during semi-solid forging and the grain refinement was attained which is considered to be favorable for improving the semi-solid formability. The grain size increased with forging temperature and decreased with forging ratio. Forging temperature has a significant effect on the precipitation behavior in grain boundary regions during the semi-solid processing. More acicular-Ti2Cu tended to precipitate in grain boundary regions with higher forging temperature and finally formed precipitates zones adjacent to grain boundaries after forged at 1,100°C. High ultimate tensile strengths and low elongation have been achieved after semi-solid forging. The strength and hardness decreased with increase of forging temperature, while the ductility increased with increase of forging ratio. The relative contributions of tensile properties were attributed to the varieties of grain size and the distribution of Ti2Cu precipitates obtained by semi-solid forging.

Abstract licence: CC BY

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.