This study presents the experimental results of the influence of mechanical fatigue on composite material. The plates of Glass fiber with SR 1500 epoxy resin with SD 2505 composite were realized by vacuum molding. Experimental tests were carried out on a standard hydraulic machine INSTRON 8516. The machine is interfaced with a dedicated computer for controlling and data acquisition. The fatigue tests were performed using sinusoidal type of waveform at a displacement control with frequency of 10 Hz. The evolution of Young’s modulus and strain based on fatigue gives us an idea about the resistance of the material. Degradation of mechanical properties was observed, and the results have showed that the Young’s modulus of plates undergo only minor changes. In fact, the residual stiffness and residual strength decrease when the cycle number of fatigue increase (100 to 50000 cycles), indicating that the studied composites have experienced some forms of mechanical damage.The mechanical tests were backed by Acoustic Emission Monitoring (AEM) during the load cycle, in order to understand the nature of the failure process in the composites such as fiber breakage, matrix crazing, matrix debonding and delamination etc.

Abstract licence: CC BY

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.