Selected-area growth of nickel micropillars on aluminum thin films by electroless plating for applications in microbolometers

An optimization process of electroless plating of nickel was carried out with NiCl2 as the nickel ion source, NaH2PO2 as the reduction agent, CH3COONa and Na3C6H5O7 as complexing agents. Electroless plated nickel layers on sputtered aluminum corning glass substrates with a resistivity of about 75.9 μΩ cm and a nickel concentration higher than 93% were obtained. This optimum process was successfully applied in growing nickel micropillars at selected areas with a well-controlled height. The microstructure of the masking layers was fabricated by means of optical photolithography for subsequent growth of nickel micropillars on selected areas. Micropillars size was defined by the opening size and the height was controlled by adjusting the plating time at a growth rate of 0.41 μm/min. This result shows that electroless nickel plating could be a good candidate for growing micropillars for applications in microbolometers.

Abstract licence: CC BY-NC-ND

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.