Effect of cotton nanocrystals on corrosion resistance and properties of electrodeposited Cu-Sn coatings

Cu–Sn electrodeposited coatings are widely used for decorative, corrosion-resistant, and wear-resistant purposes, especially in electronics, automotive, and aerospace industries. This study investigated the effect of cellulose nanocrystals (CNC), extracted from cotton by acid hydrolysis, as an additive at concentrations from 0 %v/v to 7.5 %v/v in a Cu–Sn electrolyte bath. The morphology, composition, and structure of the coatings were analyzed using scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM-EDS), X-ray diffraction (XRD), and roughness measurements. Wettability was evaluated through contact angle measurements. CNC incorporation led to more compact coatings with reduced roughness. Current efficiency increased with 1 %v/v and 2.5 %v/v CNC, indicating reduced energy consumption during electrodeposition. Contact angles rose from 95° to 106° and 126° with 1 %v/v and 2.5 %v/v CNC, showing enhanced hydrophobicity. Corrosion resistance was assessed in 3.5 wt% NaCl solution using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS), with the best performance and highest tin content observed at 1 %v/v CNC. Microhardness also increased with CNC addition, reaching its highest value at 7.5 %v/v. These findings highlight CNC as a low-cost and sustainable additive to enhance the properties of Cu–Sn coatings.

Abstract licence: CC BY-NC

40 more references, whose wording the paper’s licence keeps private.

A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.