Bulk Magnesium Diboride, Mechanical and Superconducting Properties
Vitali F. Nesterenko
2002
We email you when a new notice or a question about this paper appears.
Abstract
Hot Isostatic Pressing was applied to synthesize bulk samples with diameter up to 30 mm starting with Alfa Aesar magnesium diboride powder. HIPing at 2 kbar, 1000 C with cooling under pressure (DMCUP cycle) resulted in a fully dense (or low porosity) material with a sharp superconducting transition and critical current comparable with the best reported. Elastic constants were measured using method of resonant ultrasound spectroscopy. Their values for most dense samples (bulk modulus 142.5 GPa and Young's modulus 272.5 GPa) are close to theoretically predicted values for solid magnesium diboride. Porosity is resposible for lower values of elastic constants. Fracture toughness is evaluated based on measurements of microhardness and elastic constants. Upper critical field and irreversibility field are comparable with data for samples sintered at 3 GPa. Microstructural propeties of HIPed smaples are responsible for enhanced flux pinning. Method allows scaling of the size of the samples and manufacture of complex shapes.
Abstract licence: CC0
Reads
Read by people on this page
None yet.
Checked or read by AI through naulon
None yet.
A person counts once a day per paper. We keep no cookie and no address: a reader is a hash that changes every day. Any month under five reads shows no number.
Are you an author?
Is this your paper?
Claim it to add your note and be paid when agents cite it. Free.